journal of kerbala university

Abstract

In this research , effect of addition the filler material(bentonite) on electrical and thermal conductivity of matrix material(polyester resin) has been studied , the powder was prepared with a granular size less than (75μm) and was calcinated to three degrees of heat (200,400,600 οC) and was added to the matrix material after it was formed , Polyvinyl alcohol (PVA) was used as a binder material to study the properties of this material and study the effect of the percentage of filler, temperature and frequency in the value of electrical insulation , the results show increased the electrical conductivity of the composite by increasing the percentage of the filler and frequency of the electric field , also thermal conductivity was increased the temperature and decrease with increasing of weight fraction for the filler . تم في هذا البحث دراسة تأثير اضافة المادة المالئة (البنتونايت) على التوصيلية الكهربائية والحرارية للمادة الاساس (راتنج البولي استر) , حيث تم تهيئة مسحوق المادة المالئة بحجم حبيبي اقل من(75 μm) وحمصت الى ثلاث درجات حرارية (Cₒ200,400,600) وأضيفت للمادة الاساس بعد تهيئتها واستخدمت مادة كحول البولي فاينيل (PVA) كماده رابطه لدراسة الخصائص لهذه المادة ودراسة تأثير كل من نسبة المالئ ودرجة الحرارة والتردد في قيمة ثابت العزل الكهربائي , حيث ازدادت التوصيلية الكهربائية للمتراكب بزيادة نسبة الماليء وتردد المجال الكهربائي كذلك ازدادت التوصيلية الحرارية بزيادة درجة الحرارة وانخفضت مع زيادة النسبة الوزنية للماليء.