Kerbala University journal of kerbala university 1813-0410 4 2 2008 04 01 Structure and piezoelectricity in blends of PVDF films PVDF دراسة التركيب و البيزوكهربائية لأغشية من مخلوطات بوليمر 201 208 50977 EN Rajaa R. Abbas N. N. Rammo Ekram A. Al-Ajaj Journal Article 2008 12 01 The crystalline structure, band vibration and piezoelectric properties of PVDF (neat and blend) oriented in the -phase have been investigated utilizing X-ray diffraction, infrared spectroscopy and piezoelectric measurements respectively. The -phase and -phase always exist in the solvent cast films, but with fading orientation caused by the blending content of PMMA and PVAc. Miscibility in the PVDF-PVAc blend was confirmed by vibrational band shift. It was found that the piezoelectricity of PVDF blends might strongly be affected by the final crystal structure of PVDF resulted from blending process and on the nature of blending polymer. However, the magnitude of piezoelectric constant d33 was found to be decreasing with the content of blending polymer for both PVDF-PMMA and PVDF-PVAc blends. تم دراسة التركيب البلوري,اهتزاز الحزمة ,خواص البيزوكهربائية لبوليمر PVDF (النظيف و المخلوط) بطور- كاما باستخدام حيود الأشعة السينية, مطيافية الأشعة تحت الحمراء و قياسات البيزوكهربائية على التعاقب. تبين بان الطورين بطور كاما و ألفا تتواجد دائما بالأفلام المصبوبة من المذيب, و لكن توجيهها يختفي بسبب محتوى الخلط من بوليمري PMMA و PVAc. تم تثبيت قابلية الامتزاج في مخلوط PVDF-PVAc من خلال تزحزح حزمة الاهتزاز. وجد أن البيزوكهربائية لمخلوطات PVDF تتأثر بشدة بالتركيب البلوري ل PVDF الناتج من عملية الخلط و من طبيعة البوليمر المخلوط. و قد وجد بان مقدار ثابت البيزوكهربائية d33 يتناقص و بمقادير متفاوتة مع محتوى الخلط لكلا المخلوطين PVDF-PMMA وPVDF-PVAc . https://kj.uokerbala.edu.iq/article_50977_565c2d1e1c0ded050c03bd454dd769c5.pdf